ProductName:Bi-metal friction plate (Friction plate)
JF800C Bi-metal friction plate (Friction plate) is based on low carbon steel and sintered with copper alloy as a lining layer. The rolling mill roll of copper alloy layer make it has a certain degree of dense, and then make bi-metal composite plate, then processed by mechanical cutting. The low carbon steel surface is for the installation supporting face and the other copper alloy surface as  working face. 

The product is a replacement of the traditional copper-layer composite of steel products, with the advantage of low friction coefficient, strong wear-resistant and low cost , mainly used in various types of anti-wear plate of hydraulic pump and so on. 

1.Material is made from sintered copper powder on a low-carbon steel plate through rolling. 
2.Copper alloy hardness:HB60~90, steel back hardness:HB80~120 
3.Roughness of copper alloy:Ra0.4 
4. Copper alloy flatness is 0.05mm and the parallelism is 0.02mm 
when the thickness is 2.5mm and strip size is in the range of 150mm×100mm,. 
5.Friction and wear performance: test conditions :with 32 # machine oil lubrication, pressure is 3.5N/mm2, speed is 0.4m / s , test time is 3 hours, friction coef.μ ≤ 0.12, wear depth m≤ 0.02mm,test result shows that its performance is superior to copper alloy ZQSn6Zn6Pb3. 